 Double A also supplies a range of uncoated and coated sheets for the printing industry producing wood-free stock characterised by great smoothness, bulk and opacity.
Available is standard reels and folio sheet, our products are suitable for offset colour printing and converting applications such as envelopes, stationery, forms, brochures, catalogues, flyers, maps, annual reports and other general printing uses.
aA-Print +
| Basis weight, g/m2 |
57 - 61 |
67 - 71 |
76 - 82 |
86 - 92 |
95 - 103 |
115 - 123 |
| Moisture, % |
<7 |
<7 |
<7 |
<7 |
<7 |
<7 |
| Thickness, µm |
73 - 79 |
84 - 92 |
97 - 105 |
110 - 118 |
123 - 131 |
149 - 157 |
| Surface roughness TS ml/min |
75 - 125 |
75 - 125 |
75 – 150 |
75 - 150 |
100 - 175 |
125 - 200 |
| Surface roughness BS ml/min |
75 - 125 |
75 - 125 |
75 - 150 |
75 - 150 |
100 - 175 |
125 - 200 |
Water absorbancy Cobb,
g/m |
<30 |
<30 |
<30 |
<30 |
<30 |
<30 |
| Opacity, % |
>85 |
>88 |
>90 |
>92 |
>94 |
>95 |
| Brightness, % |
99 - 102 |
99 - 102 |
99 - 102 |
99 - 102 |
99 - 102 |
99 - 102 |
| Whiteness, % |
128 - 132 |
128 - 132 |
128 - 132 |
128 - 132 |
128 - 132 |
128 - 132 |
The quality specification is to be used for information only and must not be used as a legal
document.
The specification refers to an average of a composite sample withdrawn from a lot with random
sampling according to ISO 186:2002 |
Testing conditions:
Relative humidity 50%, Temp. 23 ºC
Testing methods:
Thickness measurement on single sheets
Surface roughness according to Bendtsen
Water absorbancy Cobb according to
D65-Brightness according to
Opacity according to
Whiteness according to |
ISO 187:1990
ISO 534:1988
ISO 8791-2:1990
ISO 535:1991
ISO 2470:1999
ISO 2471:1998
ISO11475:1999 |
Hi-White Card
| Basis weight , g/m2: ISO 536 |
137 - 143 |
147 - 153 |
157 - 163 |
177 - 183 |
207 - 213 |
227 - 233 |
| Moisture , %: ISO 287 |
5 - 6 |
5 - 6 |
5 - 6 |
5 - 6 |
5 - 6 |
5 - 6 |
| Thickness , mm: ISO 534 |
171 - 179 |
181 - 189 |
191 - 199 |
216 - 224 |
241 - 249 |
276 - 284 |
| Smoothness TS , sec/10cc: ISO 5627 |
> 16 |
> 16 |
> 16 |
> 16 |
> 16 |
> 16 |
| Smoothness BS , sec/10cc: ISO 5627 |
> 14 |
> 14 |
> 14 |
> 14 |
> 14 |
> 14 |
| Bending Stiffness MD , mN: ISO 2493 |
> 400 |
> 600 |
> 600 |
> 600 |
> 1000 |
> 1200 |
| Bending Stiffness CD , mN: ISO 2493 |
> 200 |
> 300 |
> 300 |
> 300 |
> 500 |
> 600 |
| Burst Strength , kPa: ISO 2759 |
252 |
270 |
288 |
324 |
378 |
414 |
| Tear Strength MD , mN: ISO 1974 |
1120 |
1200 |
1280 |
1440 |
1680 |
1840 |
| Tear Strength CD , mN: ISO 1974 |
1260 |
1350 |
1440 |
1620 |
1890 |
2070 |
| Tensile Strength MD , kN/m: ISO 1924/2 |
5.6 |
6 |
6.4 |
7.2 |
8.2 |
9.2 |
| Tensile Strength CD , kN/m: ISO 1924/2 |
2.8 |
3 |
3.2 |
3.6 |
4.1 |
4.6 |
| Opacity , %: ISO 2471 |
> 97 |
> 97 |
> 97 |
> 97 |
> 97 |
> 97 |
| Brightness , %: ISO 2470 |
> 98 |
> 98 |
> 98 |
> 98 |
> 98 |
> 98 |
| Whiteness: T 524 |
136 - 140 |
136 - 140 |
136 - 140 |
136 - 140 |
136 - 140 |
136 - 140 |
| The quality specification is to be used for information only and must not be used as a legal document. |
Test condition:
Relative humidity 50% , temp 23 °c |
ISO 187:1990 |
aA-Matt
| Basis weight, g/m2 |
97 - 103 |
112 - 118 |
126 - 134 |
155 - 165 |
| Moisture, % |
< 6 |
< 6 |
< 6 |
< 6 |
| Thickness, µm |
82 – 88 |
96 - 104 |
114 - 122 |
144 - 154 |
| Surface roughness TS, µm |
1.5 - 2.0 |
1.5 - 2.0 |
1.5 - 2.0 |
1.5 - 2.0 |
| Surface roughness BS, µm |
1.5 - 2.0 |
1.5 - 2.0 |
1.5 - 2.0 |
1.5 - 2.0 |
| Bending Stiffness MD, mN |
> 70 |
>100 |
> 150 |
> 300 |
| Bending Stiffness CD, mN |
> 35 |
> 55 |
> 75 |
> 150 |
| Gloss TS, % |
< 35 |
< 35 |
< 35 |
< 35 |
| Gloss BS, % |
< 35 |
< 35 |
< 35 |
< 35 |
| Opacity, % |
> 92 |
> 94 |
> 96 |
> 98 |
| Brightness, % |
95 - 98 |
95 - 98 |
95 - 98 |
95 – 98 |
| Whiteness |
118 -122 |
118 - 122 |
118 - 122 |
118 – 122 |
The quality specification is to be used for information only and must not be used as a legal
document.
The specification refers to an average of a composite sample withdrawn from a lot with random
sampling according to ISO 186:2002 |
Testing conditions:
Relative humidity 50%, Temp. 23 ºC
Testing methods:
Thickness measurement on single sheets
Surface roughness according to Bendtsen
Water absorbancy Cobb according to
D65-Brightness according to
Opacity according to
Whiteness according to |
ISO 187:1990
ISO 534:1988
ISO 8791-2:1990
ISO 535:1991
ISO 2470:1999
ISO 2471:1998
ISO11475:1999 |
aA-Gloss
| Basis weight, g/m2 |
112 - 118 |
126 -134 |
155 - 165 |
| Moisture, % |
< 6 |
< 6 |
< 6 |
| Thickness, µm |
87-95 |
101-109 |
128-138 |
| Surface roughness TS, µm |
0.6 - 1.0 |
0.6 - 1.0 |
0.6 - 1.0 |
| Surface roughness BS, µm |
0.6 - 1.0 |
0.6 - 1.0 |
0.6 - 1.0 |
| Bending Stiffness MD, mN |
> 100 |
> 130 |
> 250 |
| Bending Stiffness CD, mN |
> 55 |
> 70 |
> 150 |
| Gloss TS, % |
> 72 |
> 72 |
> 72 |
| Gloss BS, % |
> 72 |
> 72 |
> 72 |
| Opacity, % |
> 93 |
> 95 |
> 97 |
| Brightness, % |
96 - 98 |
96 - 98 |
96 - 98 |
| Whiteness |
118 - 122 |
118 - 122 |
118 - 122 |
The quality specification is to be used for information only and must not be used as a legal
document.
The specification refers to an average of a composite sample withdrawn from a lot with random
sampling according to ISO 186:2002 |
Testing conditions:
Relative humidity 50%, Temp. 23 ºC
Testing methods:
Thickness measurement on single sheets
Surface roughness according to Bendtsen
Water absorbancy Cobb according to
D65-Brightness according to
Opacity according to
Whiteness according to |
ISO 187:1990
ISO 534:1988
ISO 8791-2:1990
ISO 535:1991
ISO 2470:1999
ISO 2471:1998
ISO11475:1999 |
| ANTALIS (MALAYSIA) SDN BHD |
BEHN MEYER INTERNATIONAL TRADING SDN BHD |
Level 3A, Wisma Comcorp,
No. 37, Jalan Pelukis
U1/46, Section U1, Temasya Industrial Park,
40150 Glenmarie, Selangor
Malaysia.
Tel: (03)-7627 8300 (General)
(03)-7627 8330 (Carolyn)
(03)-76278336 (Prechelle)
Fax: (03)-7627 8320
|
No. 5, Jalan TP2
Taman Perindustrian Sime UEP
47600 Subang Jaya
Selangor Darul Ehsan
Malaysia
Contact: Mr. Naina Jamaluddin
E-mail: naina@behnmeyer.com.my
H/P: 019-2247450
Tel: (03)-80263380
Fax: (03)-80263356, (03)-80263355 |
No 2, Lorong Abu Siti
10400 Penang
Malaysia
Tel: (04)-227 2433
Fax: (04)-227 9230
E-mail: ks_ooi@shriro.com.my |
P2, Lot 247, Lorong Perusahaan 10
Prai Industrial Estate, 13600 Prai
Penang
Contact: Mr. Cheah Huey Yau
E-mail: cheahhy@behnmeyer.com.my
H/P : 019-4490286
Tel: (04)-3985176, 3985177
Fax: (04)-3985178
|
No 23, Jalan Mutiara Emas 7/6
Taman Mount Austin
81100 Johor Bahru, Johor
Malaysia
Tel: (07)-3531 800
Fax: (07)-3534 200
E-mail: jb.sales@antalismy.com
|
Suite 232-240 (2nd Floor)
Johor Tower, 15 Jalan Gereja
80100 Johor Bahru
Johor, Malaysia
Contact: Mr. Ivan Chuah Boon Leong
E-mail: ivanchuah@behnmeyer.com.my
H/P : 019-2765747
Tel : (07)-2230111
Fax: (07)-2242068 |
No 8, Laluan Perusahaan Menglembu 1
Kawasan Perindustrian Bandar Baru Menglembu (Zon Kledang)
Menglembu, 31450 Ipoh, Perak
Malaysia
Tel: (05)-2823 307
Fax: (05)-2826 453
E-mail: ipoh@antalismy.com |
Lot 7575, 7576 (1st Floor)
Wisma Hii Yii Ngiik
Jalan Kwong Lee Bank
93450 Kuching, Sarawak
Malaysia
Contact: Ms. Ivy Kho
E-mail: bmeyerkc@tm.net.my
H/P : 012-8838688
Tel: (082)-486235, 487876
Fax : (082)-484549 |
| |
Contact: Mr. Naina Jamaluddin
E-mail: naina@behnmeyer.com.my
H/P : 019-2247450
|
| |
Contact: Mr. Derik Gan Fwu Lin
E-mail: derikgan@behnmeyer.com.my
H/P: 019-7776283 |
|